 author = {村川, 洯 and 松岡, 輝雄 and MURAKAWA, Kiyoshi and MATSUOKA, Teruo},
 issue = {2},
 journal = {東京大学宇宙航空研究所報告},
 month = {Apr},
 note = {アルミ黄銅,チタン銅合金およびキュプロ・ニッケルの圧延板に低温焼鈍をほどこすことのたわみの塑性(K_b)におよぼす影響をしらべた.ここでしらべたキュプロニッケルは20% Niを含有していて,もしその他に2%以上のAlを含有する場合には適当な熱処理をほどこせば時効硬化を示すことがわかった., Bending plasticity (K_b) of strips of aluminum-brass, copper-titanium, alloy and cupro-nickel that were cold-rolled and then given low-temperature anneal was measured. The cupro-nickel sample that was tested in the present work contained approximately 20% Ni; the sample that contained more than 2% Al in addition to 20 % Ni showed age-hardening when properly heated-treated., 資料番号: SA0124338000},
 pages = {59--68},
 title = {<論文>アルミ黄銅,チタン銅合金,キュプロ・ニッケルの圧延板のたわみの塑性},
 volume = {1},