 note = {The bending plasticity of rolled sheets of phosphor bronze containing 4.5% Sn or 0.5% Ni, 0.3% Fe, 4.5% Sn or O.5% Fe, 4.5% Sn that were cold-rolled and then annealed at various temperatures lower than the recrystallization temperature as well as at the recrystallization temperature, has been measured. The sheets containing Ni br Fe were found to have smaller grains than those containing neither Ni nor Fe and therefore to show smaller plastic hysteresis than the latter. (Received May 21, 1952), 資料番号: SA0700643000},