@article{oai:jaxa.repo.nii.ac.jp:00034634,
 author = {NIKI, Eiji and KOHARA, Shiro and TATSUZAWA, Kiyohiko},
 issue = {9},
 journal = {東京大學航空研究所報告, Report/Aeronautical Research Institute, University of Tokyo},
 month = {Mar},
 note = {A study has been done on the iron-bonded titanium carbides. Mixtures of titanium carbide and iron powders in various compositions (10,20,30,40,50,60,70,80 and 90 pct iron by weight) were prepared. Linear shrinkage of compact was observed during sintering and optimum temperature for sintering was determined. Then test specimens were sintered and density, transverse rupture strength and hardeness were evaluated on the specimens in three different conditions; as sintered, quenched and tempered. Though some properties of iron-bonded titanium carbides are inferior to nickel-bonded titanium carbides, the promising characterisrics of iron-bonded titanium carbides of higher binder content (60-80 pct iron) are that those have hear treatability by dissolution of free carbon in titanium carbide into binder phase., 資料番号: SA2404935000},
 pages = {135--143},
 title = {Sintering and Some Properties of Iron-Bonded Titanium Carbides},
 volume = {29},
 year = {1964}
}