 note = {Effect of low temperature (20-250℃) annealing on cold-rolled sheet of brass was studied by means of bending plasticity measurement and hardness measurement. The relation between the bending plasticity and the annealing temperature is shown in Fig. 1, and the curve obtained by plotting the Vickers hardness versus the annealing temperature is shown in Fig. 2. It was found that hardening at room temperature occurs in cold-rolled sheet of brass (Fig. 3); a amall maximum of hardness occurs at 3 or 4 days after the sheet is cold-rolled; the hardness shows a small maximum at about 1 or 2 days thereafter and then gradually increases., 資料番号: SA2410165000},