@techreport{oai:jaxa.repo.nii.ac.jp:00046293,
 author = {竹下, 雅人 and 寺嶋, 寛成 and 岩崎, 祥大 and 羽生, 宏人 and 山口, 聡一朗 and Takeshita, Masato and Terashima, Kansei and Iwasaki, Akihiro and Habu, Hiroto and Yamaguchi, Soichiro},
 month = {Feb},
 note = {AP/HTPBコンポジット推進薬スラリーの粘弾性評価のために粒子間隙パラメータγを導入する．酸化剤の配合比を増やしてAP粒子の粒子間隙γを狭くすると，γ= 0.5前後においてスラリーの動的粘弾性や形状保持性が大きく変化した．この実験結果からAP粒子の稠密な粒子構造体が推進薬全体のレオロジー特性に大きく影響を及ぼす可能性が示唆される．, We propose the gap parameter γ between AP particles for viscoelasticity analysis in AP/HTPB composite propellant slurry. When the particle-gap γ of the AP particles was narrowed by increasing the amount of oxidant, the dynamic viscoelasticity and the shape-retaining property changed deeply at around γ = 0.5. This result suggests the possibility that the dense particulate structure of the AP particles greatly contributes to the rheology of the entire slurry., 形態: カラー図版あり, Physical characteristics: Original contains color illustrations, 資料番号: AA1930018007, レポート番号: JAXA-RR-19-003},
 title = {AP/HTPB系コンポジット推進薬スラリーにおける動的粘弾性と粒子間隙パラメータの関係},
 year = {2020}
}